RESUMO
The as-cast (Fe50Mn30Co10Cr10)97C2Mo1 HEA (high entropy alloy) was prepared and cold-rolled at 70%. Subsequently, annealing heat treatment at different temperatures (900 °C, 950 °C, 1000 °C) was carried out. The microstructure evolution and mechanical properties of the HEA were systematically investigated. The results showed that the HEA annealed at 900 °C and 950 °C exhibited uneven grain size and rich σ precipitation phase at grain boundaries. The grains began to grow and complete recrystallization, and no σ phases were observed in HEA annealed at 1000 °C, which resulted in a higher tensile strength of ~885 MPa and elongation of ~68% compared with other annealed HEAs. The higher volume fraction of annealing twins with 60°<111> orientation was produced in HEA annealed at 1000 °C, which enhanced the tensile strength and plasticity via the Twinning-induced plasticity (TWIP) mechanism.